Nickel 200 vs Nickel 201: the caustic service decision
Why Nickel 201 replaces Nickel 200 above about 315 C: carbon content, graphitisation risk, caustic resistance, mechanical limits and specification notes for flanges and seamless tube.
The carbon issue in plain language
Commercially pure nickel has outstanding resistance to caustic soda across the full range of concentration and temperature, which is why it is the reference material for caustic evaporators. The problem is not corrosion but metallurgy: carbon dissolved in the nickel becomes less soluble as the temperature falls, and over time at elevated temperature it precipitates as graphite along grain boundaries. The grain boundaries lose cohesion and the material becomes brittle without any visible warning.
Nickel 200 and 201 compared
| Item | Nickel 200 | Nickel 201 |
|---|---|---|
| UNS number | N02200 | N02201 |
| Nickel plus cobalt | 99.0 % minimum | 99.0 % minimum |
| Carbon | 0.15 % maximum | 0.02 % maximum |
| Recommended metal temperature | Below about 315 C | Above 315 C |
| Graphitisation risk | Significant above the limit | Greatly reduced |
| Typical annealed yield | About 150 MPa | About 100 MPa |
| Typical use | Chemical processing, electronics, food | Caustic evaporators, high temperature alkali |
Other limits worth noting
- Oxidising acids are not acceptable. Nickel has no chromium for passivity in oxidising media.
- Sulphur attack. Sulphur bearing environments at temperature form low melting nickel sulphide and should be avoided.
- Strength is low. Both grades have modest yield strength compared with alloyed nickel materials, so design thickness is usually governed by pressure rather than corrosion allowance.
- Magnetostriction and electrical use. Nickel 200 is chosen for electrical and electronic applications where its magnetic and conductivity behaviour matters.
Questions about this topic
At what temperature must I switch from Nickel 200 to Nickel 201?
The commonly applied boundary is about 315 C metal temperature. Above that, Nickel 200 is at risk of graphitisation and Nickel 201 should be specified. Confirm the limit against the governing design code for your project.
Is Nickel 201 weaker than Nickel 200?
Slightly, because the very low carbon that prevents graphitisation also provides less solid solution strengthening. In practice the difference is small and is not usually the deciding factor.
Can nickel be used for hydrochloric acid?
Only in very specific dilute, non aerated duty. For hydrochloric acid service, the nickel molybdenum alloys such as Hastelloy B-3 are the established choice.
Questions about our products
What products does Hangbo Alloy supply?
Four product families, all available in nickel-based alloys, titanium, duplex and special stainless steel: flanges, butt weld pipe fittings, elbows, and seamless tube and pipe. Flanges cover weld neck, long weld neck, slip-on, blind, socket weld, threaded and lap joint patterns. Fittings and elbows cover concentric and eccentric reducers, equal and reducing tees, caps, stub ends, and 45°, 90° and 180° returns in both long and short radius, plus 3D and 5D bends for piggable lines. Seamless tube and pipe is supplied cold drawn or hot finished from 6 mm to 630 mm outside diameter.
Which alloy grades are available for these products?
More than 90 grades are published in our grade library. The most requested are Inconel 625, 718, 600 and X-750, Hastelloy C-276, C-22 and B-2, Monel 400 and K-500, Incoloy 800H, 825 and 925, duplex 2205 and super duplex 2507, 316L, 904L and 254SMO stainless steel, and titanium Grade 2 and Grade 5. Nickel-based grades can also be supplied with VIM plus ESR double melting where cleanliness or fatigue life is critical.
What sizes, wall thicknesses and pressure classes can you supply?
Flanges run from NPS ½ to NPS 24 to ASME B16.5 and from NPS 26 to NPS 60 to ASME B16.47 Series A or B, in pressure classes 150 through 2500. Butt weld fittings and elbows run from NPS ½ to NPS 48 (DN 15 to DN 1200) in wall thickness Schedule 5S through XXS. Seamless tube and pipe covers 6 mm to 630 mm outside diameter, in random lengths of about 5 to 7 metres or fixed lengths up to 12 metres. Non-standard and intermediate sizes are quoted on request.
Which material and dimensional standards do you work to?
Forged flanges to ASTM B564, B381 and A182 with dimensions to ASME B16.5 and ASME B16.47. Butt weld fittings and elbows to ASTM B366 and A403 with dimensions to ASME B16.9 and MSS SP-43. Seamless tube and pipe to ASTM B444, B423, B622, B163, B167, B861, A312, A213 and A790. Marking follows MSS SP-25 and the applicable product standard. If your project is governed by EN, DIN, JIS or a company specification, send the document and we will confirm equivalence before quoting.
Is there a minimum order quantity?
There is no minimum for standard sizes and grades held in stock, and prototypes, spares and small trial batches are accepted. Made-to-order melts and special forgings carry a minimum weight that depends on the alloy and the route, typically from about 500 kg for special grades.
What inspection and certification is issued with the goods?
Every shipment carries an EN 10204 3.1 mill test certificate quoting the actual chemical and mechanical results for the specific heat lot, together with dimensional records and heat treatment data where applicable. Testing is carried out in house by optical emission spectrometry, tensile, impact and hardness testing, plus ultrasonic and eddy current examination, with hydrostatic pressure and intergranular corrosion testing to ASTM G28 or A262 Practice E where the specification requires it. Third party inspection by SGS or another recognised agency can be arranged, and their report is issued alongside the shipment.
What are typical lead times?
Standard stock items ship within days. Common production grades such as Inconel 625 or duplex 2205 are typically a few weeks. Special chemistries, larger forgings and items that require third party inspection take longer and are quoted individually against the requirement.
How are the products packed for export?
Flanges and fittings receive a rust preventive coating, are individually wrapped and are packed in plywood cases secured with steel banding. Tube ends are capped and bundles are strapped. Packing lists quote heat numbers so every case can be cross-checked against the mill certificate on arrival. We quote EXW, FOB, CFR, CIF and DAP, and mixed-alloy orders can be consolidated into one shipment with a single documentation package.
How do I request a quotation or a sample?
Send the grade or UNS number, the dimensions including schedule or wall thickness, the governing material and dimensional standards, quantity, any heat treatment or NDT scope and the certificate type you need; a drawing is ideal for special flanges and fittings. Email demi@nickel-alloy.com or message us on WhatsApp +86 15618279078 and we normally issue a formal quotation within 24 hours on working days. Samples and previous test reports can be arranged before the first order.
Talk to an engineer
Share your duty conditions and we will shortlist candidate alloys within one working day.